Abstrakt

Optimization of the low superheat casting process parameters for producing of thixotropic a 356 alloy feedstock

E.Y.El-Kady,T.S.Mahmoud,H.M.Zakaria, El-AwadyAttia,M.F.El-Sherbiny

In the present investigation, low superheat casting (LSC) was employed to produce A356 thixoforming feedstock with athixotropic microstructure. Optimization of the LSCprocess parameterswas carried out to obtain suitable thixotropic feedstock for thixoforming process. The TaguchiÂ’s optimization approach has been employed to examine the influence of the LSC process parameters, typically, pouring temperature and mould material on the microstructural characteristics ofA356 alloys, typically, the average size and shape factor of the primary á-Al grains. The level of significance of the parameters and optimum parameter combination were determined using analysis of variance (ANOVA) approach. Correlations for microstructural characteristics as functions of LSC process parameterswere determined. The results revealed that the mould material is the most influential parameter on both the average grain size and shape factor of the primary á-Al grains. The pouring temperature has lower effect on the aforementioned characteristics than the mould material. There is no interaction between the mould material and pouring temperature. The developed empirical model was successfully used to predict the average grain size and shape factor of the A356 alloy ingots produced using LSC. A356 ingot poured at a pouring temperature of 620 oC in the coppermould exhibited the bestmicrostructural characteristics suitable for thixoforming.